  • LGLT 2 is a premium quality, fully synthetic oil based grease using a lithium soap. Its unique thickener technology and its low viscosity base oil (PAO) provide excellent lubrication performances at low temperatures (-50°C) and extremely high speeds.

    PAO oil provides excellent performances at low operating and start-up temperatures
    Low viscosity base oil and additive package offer excellent lubricating ability and EP/AW properties even at very high-speed factor (1.6x106 n.dm)
    Low friction when operating, low bearing running temperatures
    Quiet running during operation makes it suitable for use in small electric motors
    Extremely good protection against corrosion in wet and/or humid environments
    Excellent long grease life
    Compatible with bearing seals and cages made of NBR, FKM, PTFE and PA 6.6

  • Tags: Bàn Map
Đơn vị tiền tệ
  • Số lượng:
  • Thành tiền
Technical Specifications:
  • DIN 51825 code : KP2G-50
  • NLGI consistency class : 2
  • Thickener/soap type : lithium
  • Color : beige
  • Base oil type : PAO
  • Operating temperature range, °C (°F) : -50 to 110 (-58 to 230)
  • Dropping point
    • DIN ISO 2176, °C (°F) : 180 min. (446 min.)
  • Density
    • DIN 51757 at 20 °C (68 °F), g/cm3 0,85-0,95
  • Base oil viscosity
    • 40 °C (104 °F), mm2/s : 18
    • 100 °C (212 °F),mm2/s : 4,5
  • Penetration DIN ISO 2137
    • 60 strokes, 10-1 mm : 265-295
    • 100,000 strokes, 10-1 mm : +50 max.
  • Mechanical stability
    • Roll stability, 50 hours at 80 °C, change 10-1 mm : 380 max.
    • SKF V2F test : -
  • Corrosion protection - SKF Emcor:
    • standard ISO 11007 : 0 - 1
    • water washout test : -
    • salt water test (100% seawater) : -
  • Water resistance
    • DIN 51 807/1, 3 hrs at 90 °C (194 °F) : 1 max.
  • Oil separation
    • DIN 51 817, 7 days at 40 °C (104 °F), static, % : < 4
  • Lubricating ability
    • SKF R2F, running test B at 120 °C : -
  • Copper corrosion
    • DIN 51 811, 100 °C (212 °F) : 1 max.
  • Rolling bearing grease life
    • SKF R0F test L50 life at 10 000 rpm, hrs : > 1000, 20,000 rpm at 110 °C (230 °F)
  • EP/AW performance
    • Wear scar, DIN 51350/5, 1400 N, mm : -
    • 4 ball test, welding load, DIN 51350/4, N : > 2000
  • Speed factor
    • Maximum n.dm value, for ball bearings : 1.600.000
  • Designation : LGLT 2/(pack size)